[1]王国杰,刘积丁,郑建岚.自密实混凝土自生约束收缩下应力松弛性能研究[J].防灾减灾工程学报,2019,39(01):82-88.[doi:10.13409/j.cnki.jdpme.2019.01.012]
 WANG Guojie,LIU Jiding,ZHENG Jianlan.Study on the Stress Relaxation Properties Induced in Restrained Autogenous Shrinkage of Self-compacting Concrete[J].Journal of Disaster Prevention and Mitigation Engineering,2019,39(01):82-88.[doi:10.13409/j.cnki.jdpme.2019.01.012]
点击复制

自密实混凝土自生约束收缩下应力松弛性能研究()
分享到:

防灾减灾工程学报[ISSN:1672-2132/CN:32-1695/P]

卷:
39卷
期数:
2019年01期
页码:
82-88
栏目:
论文
出版日期:
2019-02-28

文章信息/Info

Title:
Study on the Stress Relaxation Properties Induced in Restrained Autogenous Shrinkage of Self-compacting Concrete
文章编号:
1672-2132(2019)01-0082-07
作者:
王国杰12 刘积丁3 郑建岚12
1.福建江夏学院工程学院, 福建 福州 350108; 2.福建省环保节能型高性能混凝土协同创新中心, 福建 福州 350108; 3.国网福建省电力有限公司宁德供电公司,福建 宁德 352100
Author(s):
WANG Guojie12 LIU Jiding3 ZHENG Jianlan12
1.School of Engineering, Fujian Jiangxia University, Fuzhou 350108, China; 2.Fujian Province Collaborative Innovation Center for Environment-Friendly and Energy-Saving High Performance Concrete, Fuzhou 350108, China; 3.State Grid Fujian Ningde Electric Power Supply Company, Ningde 352100,China
关键词:
自密实混凝土 自生收缩 圆环法 约束收缩 应力松弛
Keywords:
self-compacting concrete(SCC) autogenous shrinkage ring test restrained shrinkage stress relaxation
分类号:
TU443
DOI:
10.13409/j.cnki.jdpme.2019.01.012
文献标志码:
A
摘要:
以水胶比、胶凝材料用量为主要参数,研究较长龄期内自密实混凝土的自由自生收缩性能及圆环约束收缩下钢环应变的发展规律,通过分析得到自密实混凝土在自生约束收缩下的应力松弛性能。结果表明:自密实混凝土自生变形在经过1 d左右的小幅膨胀后开始收缩,3~7 d内收缩增长较快,接下来在长达100 d的测试过程中缓慢而持续地增长; 自生收缩在受约束时应力增长也有类似的规律。自生约束收缩引起的应力松弛主要发生在3~7 d的早龄期,之后应力松弛的增长几乎停滞; 自密实混凝土的应力松弛率随水胶比的提高显著增大,随胶结料用量的增加有增大的趋势。
Abstract:
Internal stress development and stress relaxation induced by restrained autogenous shrinkage of self-compacting concrete(SCC)were investigated under different water/binder ratios and different amounts of cementitious material.Test results show that the free autogenous deformation expanded within 1 d and then shrank rapidly from 3 d to 7 d; afterward, the autogenous shrinkage grew slowly and steadily.The development of stress during restrained autogenous shrinkage also had a similar trend.The stress relaxation mainly developed at early ages within 7 d, and then its growth was almost stagnant.The stress relaxation rate of SCC increased significantly with the increase of water/binder ratio; it also increased with increasing cementitious contents.

参考文献/References:

[1] Dong W, Zhou X, Wu Z.A fracture mechanics-based method for prediction of cracking of circular and elliptical concrete rings under restrained shrinkage[J].Engineering Fracture Mechanics, 2014, 131: 687-701.
[2] 李 飞.混凝土早期约束应力发展与松弛过程研究[D].北京:清华大学, 2009.
Li F.Research on the development of restraint stress and relaxation of concrete at early age[D].Beijing: Tsinghua University, 2009.(in Chinese)
[3] 王辉明.自密实混凝土圆环约束收缩试验研究[D].福州:福州大学, 2010.
Wang H M.Exprimental study on restrained shrinkage of self-compacting concrete by ring test [D].Fuzhou: Fuzhou University, 2010.(in Chinese)
[4] Hossain A B, Weiss W J.Assessing residual stress development and stress relaxation in restrained concrete ring specimens[J].Journal of Cement & Concrete Composites, 2004, 26: 531-540.
[5] Dally J W, Riley W F.Experimental stress analysis[M].3rd ed.New York:McGraw Hill, 1991.
[6] 普通混凝土长期性能和耐久性能试验方法标准:GB/T 50082—2009 [S].北京:中国建筑工业出版社,2009.
Standard for test methods of long-term performance and durability of ordinary concrete: GB/T 50082—2009 [S].Beijing: China Architecture & Building Press,2009.(in Chinese)
[7] Standard test method for determining age at cracking and induced tensile stress characteristic of mortar and concrete under restrained shrinkage: ASTM C 1581—04 [S].West Conshohocken,PA: ASTM International, 2004.
[8] 王国杰.自密实混凝土早龄期收缩、开裂性能研究[D].福州:福州大学, 2011.
Wang G J.Shrinkage and cracking performance of self-compacting-concrete at early age[D].Fuzhou: Fuzhou University, 2011.(in Chinese)
[9] 刘积丁.自密实混凝土自生约束收缩下应力松弛性能研究[D].福州:福州大学, 2017.
Liu J D.Study on the stress relaxation properties of self-compacting concrete under autogenous shrinkage[D].Fuzhou:Fuzhou University,2017.(in Chinese)

备注/Memo

备注/Memo:
收稿日期:2017-11-20; 修回日期:2018-01-24 基金项目:国家自然科学基金项目(51578153)、福建省教育厅科研项目A类产学研项目(JA15529)资助 作者简介:王国杰(1970-),女,教授,博士。主要从事结构工程研究。Email:wangguojie@fzu.edu.cn
更新日期/Last Update: 2019-02-20